The following chart shows typical end-of-life conditions and possible solutions to improve tool life.

 

Carbide Fracture

Problem: Carbide Fracture

Possible Cause

  • Hard cutting conditions
  • Extreme impact

Recommended Solution

  • Contact your Kennametal Sales Representative for a full evaluation.

 

Thermal Cracking

Problem: Thermal Cracking

Possible Cause

  • Hard cutting conditions
  • Lack of penetration
  • Grinding of material not conveyed
  • Excessive heat generation during cutting

Recommended Solution

  • Contact your Kennametal Sales Representative for a full evaluation.

 

Excessive Carbide Wear

Problem: Excessive Carbide Wear

Possible Cause

  • Very abrasive cutting conditions
  • High rotation speed
  • Cutting too deep

Recommended Solution

  • Adjust rotation and feed of machine.

 

Steel Wash

Problem: Steel Wash

Possible Cause

  • Grinding of material not conveyed
  • Abrasive cutting conditions

Recommended Solution

  • Contact your Kennametal Sales Representative for a full evaluation.
  • NB tip, X-series, hardfacing.
  • Increase feed.
One-Sided Steel/Wear on Gage

Problem: One-Sided Steel/Wear on Gage

Possible Cause

  • Conical not rotating
  • Misaligned blocks
  • Sticky cutting conditions
  • Worn blocks
  • Excess material build-up on tool

Recommended Solution

  • Clean the conical for foreign particles.
  • Tap the conical.
  • Contact your Kennametal Sales Representative for a full evaluation.

 

Shank Breakage

Problem: Shank Breakage

Possible Cause

  • Worn block bore
  • Worn-out sleeve
  • Hard cutting conditions
  • Blunt/missing cutting tip

Recommended Solution

  • Contact your Kennametal Sales Representative for a full evaluation.

 

Shank Bending

Problem: Shank Bending

Possible Cause

  • Worn block bore
  • Worn-out sleeve
  • Hard cutting conditions
  • Blunt/missing cutting tip

Recommended Solution

  • Contact your Kennametal Sales Representative for a full evaluation.

 

Broken Hub/Hub Failure

Problem: Broken Hub/Hub Failure

Possible Cause

  • Worn-out block: lateral play

Recommended Solution

  • Contact your Kennametal Sales Representative for a full evaluation.

 

Retainer Failure

Problem: Retainer Failure

Possible Cause

  • Worn-out block: lateral play

Recommended Solution

  • Contact your Kennametal Sales Representative for a full evaluation.

 

Sleeve Breakage

Problem: Sleeve Breakage

Possible Cause

  • Hard cutting conditions
  • Worn-out sleeves

Recommended Solution

  • Contact your Kennametal Sales Representative for a full evaluation.

 

Vous êtes sur le point d’ajouter à votre page mes solutions. Souhaitez-vous continuer ?
Select the destination where you want to move à.
Nouvelle Folder
    • Applied Filters:
    • Clear All

product-image
Please adjust the following properties from

catalogue ISO

catalogue ANSI

to find similar products.

The following files are available

Please select a file to download

Models

Vous devez être connecté pour voir les informations de votre tableau de bord
Session expired due to inactivity, please login again
Le(s) produit(s) () que vous essayez d’ajouter au panier est/sont indisponible(s), veuillez Contacter le service client.
article(s) ajouté(s) avec succès au panier
View Cart

. Please enter the desired qty for the material(s) you want to include in your promotion or Proceed Without Promotion and only your base materials will be added to the cart.

Minimum quantity should be

SAP Material Numbercatalogue ISOGrade  

You are about to leave the Solution building process.

Are you sure you want to leave?